产品详情
| 品牌 |
Atlantic/大西洋 |
型号 |
ER316L |
| 牌号 |
ER316L |
类型 |
药芯焊丝 |
| 焊接方法类型 |
气保护焊丝 |
被焊材料 |
不锈钢 |
| 加工定制 |
否 |
标准直径 |
1.0-3.0mm |
| 长度 |
盘丝mm |
焊接位置 |
全位置 |
| 药芯类型 |
实芯 |
材质 |
不锈钢 |
| 焊接电流 |
90-120A |
用途 |
主要用于焊接17Cr-9Ni钢 |
| 工作温度 |
常温℃ |
产地 |
四川 |
| 是否含助焊剂 |
否 |
规格尺寸 |
1.0-3.0mm |
| 重量 |
15kg |
| ER304 | 主要用于焊接18Cr-8Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-0.45 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:0.42% |
| ||||||
| Ni:8.33% |
| ||||||
| Cr:17.10% |
| ||||||
|
|
| ||||||
| ER304L | 主要用于焊接17Cr-8Ni钢 | C:0.028% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:0.42% |
| ||||||
| Ni:8.33% |
| ||||||
| Cr:17.10% |
| ||||||
|
|
| ||||||
| ER308 | 主要用于焊接19Cr-9Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:0.42% |
| ||||||
| Ni:10.33% |
| ||||||
| Cr:20.10% |
| ||||||
| ER308L | 主要用于焊接20Cr-9Ni钢 | C:0.024% | 拉伸强度Mpa 1200 | 0.8-4.5 | 5/12.5/15/20 | 100/270/300 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:0.42% |
| ||||||
| Ni:10.33% |
| ||||||
| Cr:20.10% |
| ||||||
|
|
| ||||||
| ER309 | 主要用于焊接20Cr-13Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:0.42% |
| ||||||
| Ni:14.33% |
| ||||||
| Cr:20.10% |
| ||||||
| ER309L | 主要用于焊接20Cr-14Ni钢 | C:0.024% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:0.42% |
| ||||||
| Ni:14.33% |
| ||||||
| Cr:20.10% |
| ||||||
|
|
| ||||||
| ER309Lsi | 主要用于焊接20Cr-14Ni钢 | C:0.024% | 拉伸强度Mpa1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:1.02% |
| ||||||
| Ni:14.33% |
| ||||||
| Cr:20.10% |
| ||||||
| ER321 | 主要用于焊接16Cr-7Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:0.42% |
| ||||||
| Ni:8.33% |
| ||||||
| Cr:17.10%Ti0.73 |
| ||||||
| ER347 | 主要用于焊接16Cr-9Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 0 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:0.42% |
| ||||||
| Ni:9.33% |
| ||||||
| Cr:17.10% |
| ||||||
| （Ta+Nb）（10*C）-10 |
| ||||||
| ER347L | 主要用于焊接17Cr-9Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 0 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:0.42% |
| ||||||
| Ni:9.33% |
| ||||||
| Cr:17.10% |
| ||||||
| （Ta+Nb）（10*C）-10 |
| ||||||
| ER316 | 主要用于焊接16Cr-9Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
| Mn:1.65% | TIG:1.0-4.5 | ||||||
| Si:0.42% |
| ||||||
| Ni:10.33% |
| ||||||
| Cr:17.10% |
| ||||||
| Mo2.03 |
| ||||||
| C:0.064% | MIG:0.8-1.6 | ||||||
 | |||||||
|
| |||||||
|
| |||||||
|
| |||||||
|
| |||||||
|
| |||||||
|
| |||||||